Research of Calcium Phosphates Using Fourier Transform Infrared Spectroscopy

In the biomaterial research field, nowadays a great attention is driven onto calcium phosphates synthesis and obtaining of ceramics that can be used in orthopedics and dentistry, in the form of coatings, granules, porous or solid blocks, as well as in the form of various composite materials. The most frequently studied, clinically tested and used synthetic materials based on calcium phosphate (CaP) are hydroxyapatite [HAp Ca10(PO4)6(OH)2], ┚-tricalcium phosphate [┚-TCP Ca3(PO4)2] and biphasic HAp/┚-TCP mixture. CaP ceramic demonstrates high biocompatibility and bioactivity while it contacts bone cells, builds a direct chemical connection between bone tissues and ceramic implant. As practice shows, purchased materials, most often commercial CaP materials, not always have properties and qualities defined by the manufacturer. Frequently, the manufacturer’s information about the offered product is not complete or precise, by it troubling usage of raw CaP material for development of implants. The most common imperfections of CaP materials are – unpredictable properties after the high temperature treatment (composition and clarity of crystal phases, chemical composition, thermal stability, etc.) which become clear only after the high temperature treatment of the ready implant material has occurred. For several years, Riga Biomaterial Innovation and Development Centre (RBIDC) of Riga Technical University perform a wide range of property studies of various commercial CaP raw materials.